Shanglin Science and Technology

Adhesive for body

Product Model PVC232 KSJ378 MF226 GZ375
Appearance White fine homogeneous paste gray fine homogeneous colloid Black/White Homogeneous Colloid black homogeneous colloid
Density (g/cm3) ≤ 1.6 ≤1.5 1.3～1.5 1.3～1.5
Not volatile (%) ≥95 ≥90 ≥95 ≥95
Viscosity 5,000~20,000 cps ≤ 6,000 CPS ≥ 50(g/min, room temperature 3mm 0.4MPa) ≥ 50(g/min, room temperature 3mm 0.4MPa)
Liquidity (mm) Horizontal, vertical ≦ 5 Horizontal, vertical ≦ 5 Horizontal, vertical ≦ 5 Horizontal, vertical ≦ 5
Curing conditions 140 ℃ * 30min 140 ℃ * 30min 180 ℃ * 20min 180 ℃ * 20min
Shear strength (MPa) ≥ 0.8 / ≥ 0.8 ≥0.5
Adhesion Adhesion Strength> Cohesive Strength Adhesion Strength> Cohesive Strength No slippage and wire drawing (oil surface adhesion) No slippage and wire drawing (oil surface adhesion)
Expansion rate (%) / / / ≥30
Stone impact resistance (10 cycles) / Average retention of coating ≥ 96%, no bottom exposure / /
Polyurethane structural adhesive PU563 Project Performance
Appearance Black, homogeneous paste
Degreaser (g/cm³) 1.35±0.05
Sag (mm) 0
Table dry time (min) 20～60
Curing speed (mm/d) 1～3
Volatile (%) ≤4
Shore hardness (Shore-A) 60±5
Tensile strength (MPa) ≥ 4.5
Elongation at break (%) ≥ 400
Extrudability (ml/min) ≥80
Construction temperature range (℃) 5～ 35
Working temperature (℃) -40～90